AWARD WINNING SPECIALIST

Combustion Controls Solutions & Environmental Services, Inc. is the best choice for turnaround work as well as routine repairs. Below are summaries for some of the services we offer that we feel are all part of completing projects in a thorough and complete manner:

• We offer up front budget analysis packages, complete with scheduling, cost breakdowns, complete material evaluation and heat transfer analysis at no cost to the customer. We also offer refractory design & engineering at the customer's request. This service allows the customer to gather & provide more information to help us all make better and more efficient decisions for the new competitive environment we work in today.

• We offer unsurpassed experience in installation methods, turnaround planning and current products used in units throughout the industry.

• During projects / turnarounds we provide the customer up to date information on cost, scheduling progress and any potential roadblocks that might impact the time frame or cost of the turnaround / project. We take pride in meeting our budgets and scheduled deadlines, as well as submitting suggestions for alternative solutions to problems that are encountered during schedule driven projects such as turnarounds.

• We offer the most experienced group of refractory managers and well trained installation craftsmen that can be found in the refractory industry anywhere in the world. Our goal is to maintain constant improvement for our craftsmen and our management team.

• We keep complete as built drawings during project execution and at the completion of a job we have the changes incorporated into the existing drawings. We build new drawings and provide the customer with vellums for their files. We can provide our customers with the drawings on floppy disk in the format requested by the customer, saving money for our customers by eliminating the need to hire computer draftsman to update your drawings electronically.

• We have a complete and comprehensive Quality Control Program that is continually modified to incorporate the latest technology, new products and installation methods that are developed. We work closely with the customers engineering departments developing some of the new methods mentioned above.

What refractories are, different types of refractories, properties of refractories, and applications/use of them.

Basic refractories were so named because they exhibit resistance to corrosive reactions with chemically basic slags, dusts and fumes at elevated temperatures. Some classes of basic refractories have been developed that exhibit excellent resistance to rather acidic slags.

Broadly speaking, basic refractories generally fall into one of five compositional areas:

1. Products based on deadburned magnesite or magnesia.

2. Products based on deadburned magnesite or magnesia in combination with chrome-containing materials such as chrome ore.

3. Deadburned magnesite or magnesia in combination with spinel.

4. Deadburned magnesite or magnesia in combination with carbon.

5. Dolomitic products.

Basic Refractory Raw Materials - The principal raw materials used in the production of basic refractories are dead-burned and fused magnesites, dead-burned dolomite, chrome ore, spinel and carbon. In recent years, the trend has shifted to developing highly engineered basic refractories. One result of this effort has been the development of technology to address specific wear mechanisms by employing special additives to the refractory composition. These additives generally constitute less than 6% of the total mix, although levels at 3% and below are probably the most common.

High-Alumina Refractories -The term high-alumina brick refers to refractory brick having an alumina content of 47.5% or higher. High-alumina brick are classified by their alumina content according to the following ASTM convention. The 50%, 60%, 70% and 80% alumina classes contain their respective alumina contents with an allowable range of plus or minus 2.5%.

Mullite brick - predominantly contains the mineral phase mullite.

Chemically-bonded brick - usually phosphate-bonded brick in the 75% to 85% alumina range. An aluminum orthophosphate bond can be formed at relatively low temperatures.

Alumina-chrome brick - typically formed from very high purity, high-alumina materials and chromic oxide. At high temperatures, alumina and chromia form a solid solution which is highly refractory.

Alumina-carbon brick - high-alumina brick (usually bonded by a resin) containing a carbonaceous ingredient such as graphite.

Fireclay Refractories - Refractory fireclay consists essentially of hydrated aluminum silicates with minor proportions of other minerals. There are 5 standard classes of fireclay brick: superduty, high-duty, medium-duty, low-duty, and semi-silica. These classes cover the range from approximately 18% to 44% alumina, and from about 50% to 80% silica.

Superduty - these bricks have good strength and stability of volume at high temperatures and an alumina content of 40% to 44%. Some superduty brick have superior resistance to cracking or spalling when subjected to rapid changes of temperature.

High-duty - these bricks are used in large quantities and for a wide range of applications. Because of their greater resistance to thermal shock, high-duty fireclay brick can often be used with better economy than medium-duty brick for the linings of furnaces operated at moderate temperatures over long periods of time but subject to frequent shutdowns.

Medium-duty - these bricks are appropriate in applications where they are exposed to conditions of moderate severity. Medium-duty brick, within their serviceable temperature ranges, can withstand abrasion better than many brick of the high-duty class.

Low-duty - these brick find applications as backing for brick with higher refractoriness, and for other service where relatively moderate temperatures prevail.

Silica Refractories - Silica refractories are well adapted to high-temperature service because of their high refractoriness, high mechanical strength and rigidity at temperatures almost up to their melting points, as well as their ability to resist the action of dusts, fumes, and acid slags. Silica brick are divided into Type A and Type B based on the brick's flux factor.

Monolithic Refractories - Monolithic or monolith-forming refractories are special mixes or blends of dry granular or cohesive plastic materials used to form virtually joint-free linings.

Types of Monolithic Refractories

Plastic Refractories
Ramming Mixes
Gunning Mixes
Castables

Properties of Refractories - Important properties of refractories which can be determined most readily are chemical composition, bulk density, apparent porosity, apparent specific gravity and strength at atmospheric temperatures. These properties are often among those which are used as controls in the manufacturing and quality control process. The chemical composition serves as a basic for classification of refractories. The density, porosity and strengths of fired products are influenced by many factors. Among these are type and quality of the raw materials, the size and "fit" of the particles, moisture content at the time of pressing, pressure of pressing, temperature and duration of firing, kiln atmosphere and the rate of cooling.

Abrasion of Refractories: Wearing away of the surfaces of refractory bodies in service by the scouring action of moving solids.

Acid-Proof Brick: Brick having low porosity and permeability, and high resistance to chemical attack of penetration by most commercial acids and some other corrosive chemicals.

Alumina: The oxide of aluminum; melting point 3720°F (2050°C); in combination with water, alumina forms the minerals diaspore, bauxite and gibbsite. In combination with silica and water, alumina forms kaolinite and other clay minerals.

Castable Refractory: A mixture of a heat-resistant aggregate and a heat-resistant hydraulic cement. For use, it is mixed with water and rammed, cast or gunned into place.

Gunning: The application of monolithic refractories by means of air-placement guns.

Insulating Refractories: Lightweight, porous refractories with much lower thermal conductivity and heat-storage capacity than other refractories. Used mostly as backing for brick or higher refractoriness and higher thermal conductivity. These materials provide fuel economy through lower heat losses, increased production due to shorter heat-up time, economy of space (size and weight) because of thinner walls and improved working conditions. Insulating refractories are available as brick or monoliths.

Plastic Refractory: a blend of ground refractory materials in plastic form, suitable for ramming into place to form monolithic linings.

Refractories: Nonmetal materials suitable for use at high temperatures in furnace construction. While their primary function is resistance to high temperature, they are usually called on to resist other destructive influences such as abrasion, pressure, chemical attack and rapid changes in temperature.

Silica: The oxide of silicon. Quartz and chalcedony are common silica materials; quartzite, sandstone and sand are composed largely of free silica in the form of quartz.